Rezults of investigation of metals rheology under high temperature plastic deformations




The work has been carried out to development and improvement of methods of implementation of plastometric test of
samples for investigation rheology of metals under high temperature plastic deformation. Test series of samples from austenitic
stainless steel 08X18H10T and AMg6 alloy have been carried out. Metals microstructure at backend of deformation
process in different area of deformation site of sample has been studied using metallographic analysis. New result
which indicates sharp growth grain under small strain deformation has been obtained. Definition intermetal hardness experiments
for AMg6 alloy have been carried out. The adequacy of developed earlier rheological model describing processes
recovery and dynamic recristallization for elastic-visco-plastic environment has been confirmed upon large quantity
experimental dates.

Результаты исследований реологии металлов при больших высокотемпературных пластических деформациях.

Выполнены работы по развитию и совершенствованию методики проведения пластометрических испытаний образцов для исследования реологии металлов при больших высокотемпературных пластических деформациях.
Проведена серия испытаний образцов из нержавеющей стали 08Х18Н10Т и сплава АМг6. Методами количественной металлографии исследована структура металлов на конечной стадии деформации в разных зонах очага
деформации образца. Получен новый результат, свидетельствующий о резком росте зерен при малой степени де-
формации. Выполнены эксперименты по определению твердости интерметаллидов, выделяемых в сплаве АМг6
при пластической деформации. На большом количестве экспериментальных данных подтверждена адекватность
построенной ранее реологической модели, описывающей процессы возврата и динамической рекристаллизации в
определяющих соотношениях для упруговязкопластической среды.